Stainless Hlau Round Bars tuaj nyob rau hauv ntau qib uas siv nyob rau hauv ntau yam lag luam.Stainless hlau puag ncig tuav yog siv vim lawv lub zog thiab kev tiv thaiv corrosion.Chromium muaj nyob rau hauv tag nrho cov hlau stainless.Stainless Hlau Round Bars tuaj nyob rau hauv diameters li ntawm 4mm mus rau 500mm.Qhov ntev ntawm cov tuav yog li ntawm 1 mus rau 6 meters.Tseem muaj kev cai loj thiab ntev muaj.Peb kuj yog cov chaw muag khoom ntawm Stainless Hlau 304 Round Bars, Stainless Hlau 304L Round Bars, Stainless Hlau 316 Round Bars, thiab lwm yam.
| Stainless hlau Bar Length | 2 mus rau 6 meters los yog 8 mus rau 20 ko taw |
| Stainless hlau qws Chamfering | Muaj nyob rau hauv 30, 45 & 60 degrees los ntawm lub siab tsis siv neeg ob-kawg chamfering tshuab |
| Ultrasonic Test ntawm ASTM A276 Threaded Qws | Raws li ASTM A-388, EN 10308 (chav kawm 1 txog 4), API 6A / ISO yog 100% kuaj los ntawm Digital Ultrasonic Flaw Detector, 10423: 2003-PSL 3, MIL-STD 2154, SEP 1920: 1984 |
| Stainless Hlau Round Bar Loj Tolerances | h11 ua |
| Tolerance ntawm Txias Rolled SS Round Bar Length | Tshuag nyob rau hauv tshwj xeeb txiav rau ntev bar nyob rau hauv kam rau ua - 0 / + 10mm (-0 + 0.5 nti) |
| Nto tiav ntawm Cold Rolled SS Round Bar | Txias rub los yog Belt polished mob |
| Round Bar Kev kho cua sov | Annealed thiab Solution Annealed |
| Qib | Elongation | Qhov ntom | Tensile zog | Yield zog (0.2% Offset) | Melting Point |
| SIB 202 | 40% | 8.0 g / cm3 | 515 MPa ua | 275 MPa rau | 1454 ° C (2650 ° F) |
| SIB 303 | 50% | 55% | Psi – 85,000 | Psi – 45,000 | RWB 180 |
| SIB 304 | 40% | 8.0 g / cm3 | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 1400 ° C (2550 ° F) |
| SWB 304L | 40% | 8.0 g / cm3 | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 1400 ° C (2550 ° F) |
| SIB 316 | 35% | 8.0 g / cm3 | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 1454 ° C (2650 ° F) |
| SWB 316L | 40% | 8.0 g / cm3 | 485 Min | 170 Min. | 1400 ° C (2550 ° F) |
| ASTM Qib | Cov pa roj carbon | Manganese | Silicon | Sulfur | Phosphorous | Chromium | Nickel | Molybdenum | Lwm yam |
| 304 | 0.08 max | max 2.00 Nws | 0.75 max | 0.030 max | 0.045 max | 18.0-20.0 Nws | 8.0 11.0 Nws | - | - |
| 316 | 0.08 max | max 2.00 Nws | 0.75 max | 0.030 max | 0.045 max | 16.0-18.0 Nws | 10.0 14.0 Nws | 2.0 3.0 | - |
| 317l ua | 0.035 max | max 2.00 Nws | 0.75 max | 0.030 max | 0.045 max | 18.0-20.0 Nws | 11.0 14.0 Nws | 3.0 4.0 | - |
| 310 S ib | 0.08 max | max 2.00 Nws | 1.5 max | 0.030 max | 0.045 max | 24.0-26.0 Nws | 19.0 22.0 Nws | 3.0 4.0 | - |
| 347 h ua | 0.04 0.10 Nws | max 2.00 Nws | 0.75 max | 0.030 max | 0.045 max | 17.0-19.0 Nws | 9.0 13.0 Nws | - | 10C(Cb+Ta) <1.10% |
| 321 | 0.08 ib | max 2.00 Nws | 0.75 max | 0.030 max | 0.045 max | 17.0-20.0 Nws | 9.0 12.0 Nws | - | 5C 0.70% |
| Txoj kab uas hla | Daim ntawv luj | Dia | Daim ntawv luj |
| (mm) | ib ' meter ' (kg) | (hauv) | ib ' meter ' (kg) |
| 3mm ib | 0.06 ib | 1/8 " | 0.06 ib |
| 4mm ib | 0.10 | 3/16 " | 0.14 ib |
| 5mm ib | 0.16 | 1/4 " | 0.25 |
| 6mm ib | 0.22 | 5/16 " | 0.39 ib |
| 7mm ib | 0.30 Nws | 3/8 " | 0.56 ib |
| 8mm ib | 0.40 Nws | 7/16 " | 0.77 ib |
| 10 hli | 0.62 ib | 1/2 " | 1.00 Nws |
| 12 hli | 0.89 ib | 9/16 " | 1.22 |
| 14mm ib | 1.22 | 5/8 " | 1.56 ib |
| 15 hli | 1.40 Nws | 11/16 " | 1.89 ib |
| 16 hli | 1.59 ib | 3/4 " | 2.25 |
| 18 hli | 2.01 Nws | 7/8 " | 3.07 Nws |
| 20 hli | 2.48 ib | 1 ″ | 4.03 ib |
| 22 hli | 3.00 Nws | ||
| 24mm ib | 3.57 ib | ||
| 25 hli | 3.88 ib |